ASTM A199/A199M-92 Heat-Exchanger tubes,Condenser Tubes

ASTM A199, ASTM A199 T11, ASTM A199 T22, ASTM A199 T5, boiler tube, heat exchanger tubes

ASTM A199/A199M-92 Specification for Seamless Cold-Drawn Intermediate Alloy-Steel Heat-Exchanger tubes and Condenser Tubes.  The ASTM A119 pressure boiler tube is wrapped with nylon fabric then bundled with 2 steel strips in each end, and other 2 in the middle.

Main grade we supply for ASTM A199

• ASTM A199 T11

• ASTM A199 T22

• ASTM A199 T5




Delivery Condition:




• Heat treatment,Annealed, Normalized, Normalized and Tempered




Surface treatment:




• Oil-dip, Varnish, Passivation, Phosphating, Shot Blasting

• Painting as requested.




Chemical analysis of ASTM A199 (%):

Steel grade	WT	C	Mn	P (max)	S (max)	Si	Cr	Mo
ASTM A199/T4	MW	0.15MAX	0.30-0.60	0.03	0.03	0.50-1.00	2.15-2.85	0.44-0.65
ASTM A199/T5	MW	0.50-0.15	0.30-0.60	0.03	0.03	0.50MAX	4.00-6.00	0.45-0.65
ASTM A199/T7	MW	0.15MAX	0.30-0.60	0.03	0.03	0.50-1.00	6.00-8.00	0.45-0.65
ASTM A199/T9	MW	0.15MAX	0.30-0.60	0.03	0.03	0.25-1.00	8.00-10.0	0.90-1.10
ASTM A199/T11	MW	0.50-0.15	0.30-0.60	0.03	0.03	0.50-1.00	1.00-1.50	0.44-0.65
ASTM A199/T22	MW	0.50-0.15	0.30-0.60	0.03	0.03	0.50MAX	1.90-2.60	0.87-1.13

* Ni 0.40 max; V 0.18-0.25; Cb 0.06-0.10; N 0.03-0.07; Al 0.04 max

Mechnical Properties of ASTM A199:

Steel grade	Tensile Strength (Mpa)	Yield Strength (Mpa)	Elongation (%)	SPECIFIC REQUIREMENT
ASTM A199/T4	415MIN	170MIN	30/22	Hardness 85 HRB MAX
ASTM A199/T5	415MIN	170MIN	30/22	Hardness 85 HRB MAX
ASTM A199/T7	415MIN	170MIN	30/22	Hardness 85 HRB MAX
ASTM A199/T9	415MIN	170MIN	30/22	Hardness 85 HRB MAX
ASTM A199/T11	415MIN	170MIN	30/22	Hardness 85 HRB MAX
ASTM A199/T22	415MIN	170MIN	30/22	Hardness 85 HRB MAX

Usage:

Steel pipe are ubiquitous and can be found underground and within residential walls, laboratories, and commercial and industrial structures. Seamless steel pipe transport fluids including water, natural gas, waste and air. Three manufacturing methods exist to produce steel pipes.

Seamless steel pipes are produced using an extrusion mold. Welded steel pipes are produced by rolling a sheet of steel into a tube and welding the seam. Seamless steel pipes are less expensive. The third method is casting. Molten steel is poured into a casting mold.

Our steel pipes and tubes are the preferred choice for processes under the following conditions:

- high temperatures

- and/or high pressure


We have a team of experienced professionals with years of experience in manufacturing.




•